CYANOACRYLATE ADHESIVES
Super glue
METHYL GRADE
|
GRADE
|
CHEMICAL COMPOSITION
|
SPECIFIC GRAVITY
20°C g/ml
|
VISCOSITY
20°C mPa.s
|
GAP FILLING
microns
|
SPEED OF BONDING
|
TENSILE STRENGTH
DIN 53288
N/mm²
|
SHEAR STRENGTH
DIN 53283
N/mm²
|
IMPACT STRENGTH
ASTM D 950
N.mm/mm²
|
|
10
|
METHYL
|
1,10
|
5 - 10
|
10 - 40
|
2
|
25 - 30
|
20 - 25
|
10 - 15
|
|
14
|
METHYL
|
1,15
|
100 - 150
|
10 - 100
|
2
|
25 - 30
|
20 - 25
|
10 - 15
|
|
17
|
METHYL
|
1,19
|
1100 - 1600
|
10 - 200
|
1
|
25 - 30
|
20 - 25
|
10 - 15
|
Relative setting time : 5 = highest speed, 1 = lowest speed.
ETHYL GRADE
|
GRADE
|
CHEMICAL COMPOSITION
|
SPECIFIC GRAVITY
20°C g/ml
|
VISCOSITY
20°C mPa.s
|
GAP FILLING
microns
|
SPEED OF BONDING
|
TENSILE STRENGTH
DIN 53288
N/mm²
|
SHEAR STRENGTH
DIN 53283
N/mm²
|
IMPACT STRENGTH
ASTM D 950
N.mm/mm²
|
|
20
|
ETHYL
|
1,05
|
1 - 5
|
10 - 40
|
4
|
12 - 25
|
15 - 25
|
13 - 18
|
|
23
|
ETHYL
|
1,06
|
40 - 80
|
10 - 60
|
3
|
18 - 25
|
13 - 18
|
13 - 18
|
|
25
|
ETHYL
|
1,07
|
300 - 500
|
10 - 150
|
2
|
18 - 23
|
13 - 18
|
15 - 20
|
|
27
|
ETHYL
|
1,08
|
1200 - 1800
|
10 - 200
|
2
|
18 - 25
|
13 - 18
|
13 - 18
|
|
29
|
ETHYL/BLACK
|
1,08
|
1000 - 1500
|
10 - 200
|
1
|
18 - 25
|
13 - 18
|
13 - 18
|
|
32
|
ETHYL
|
1,05
|
10 - 20
|
10 - 40
|
5
|
18 - 25
|
13 - 18
|
13 - 18
|
|
34
|
ETHYL
|
1,06
|
30 - 60
|
10 - 100
|
5
|
18 - 25
|
13 - 18
|
13 - 18
|
|
41
|
ETHYL
|
1,05
|
20 - 50
|
10 - 40
|
5
|
18 - 25
|
13 - 18
|
15 - 20
|
|
43S
|
ETHYL
|
1,06
|
100 - 150
|
10 - 150
|
4
|
22 - 25
|
15 - 20
|
15 - 20
|
|
43
|
ETHYL
|
1,06
|
100 - 150
|
10 - 150
|
4
|
22 - 25
|
15 - 20
|
15 - 20
|
|
45
|
ETHYL
|
1,08
|
800 - 1200
|
10 - 200
|
4
|
22 - 25
|
15 - 20
|
15 - 20
|
|
47
|
ETHYL / GEL
|
1,10
|
15000-40000
|
10 - 400
|
2
|
12 - 25
|
18 - 26
|
10 - 20
|
|
54
|
ETHYL / HIGH TEMP.
|
1,05
|
25 - 50
|
10 - 60
|
4
|
18 - 25
|
13 - 18
|
13 - 18
|
Relative setting time : 5 = highest speed, 1 = lowest speed.
ALCOXY GRADE
|
GRADE
|
CHEMICAL COMPOSITION
|
SPECIFIC GRAVITY
20°C g/ml
|
VISCOSITY
20°C mPa.s
|
GAP FILLING
microns
|
SPEED OF BONDING
|
TENSILE STRENGTH
DIN 53288
N/mm²
|
SHEAR STRENGTH
DIN 53283
N/mm²
|
IMPACT STRENGTH
ASTM D 950
N.mm/mm²
|
|
60
|
ALCOXY
|
1,06
|
4 - 10
|
10 - 40
|
2
|
10 - 25
|
14 - 22
|
15 - 20
|
|
61
|
ALCOXY
|
1,06
|
20 - 40
|
10 - 40
|
2
|
10 - 20
|
14 - 22
|
15 - 20
|
|
63
|
ALCOXY
|
1,07
|
100 - 150
|
10 - 150
|
1
|
10 - 25
|
14 - 22
|
15 - 20
|
|
67
|
ALCOXY
|
1,06
|
1100-1600
|
10 - 250
|
2
|
12 - 22
|
14 - 22
|
15 - 20
|
Relative setting time : 5 = highest speed, 1 = lowest speed.
PHYSICAL PROPERTIES
| FLASH POINT ISO 2592 ( °C ) |
87 |
| OPERATING TEMPERATURE ( °C ) |
-50 +80 * IST54 UP TO 125°C |
| SOFTENING RANGE ( °C ) |
160/170 |
| REFRACTIVE INDEX n sup.20 sub.D |
SIMILAR TO GLASS |
| ELECTRICAL RESISTIVITY DIN 53482 ( OHM x mm ) |
>10 E 15 |
| DIELECTRIC STRENGTH DIN 53481 ( Kv/mm ) |
25 |
| DIELECTRIC CONSTANT DIN 53483 ( 1 MHz ) |
5,2 |