ACRYLIC STRUCTURAL ADHESIVES
AT CHEMICAL ACTIVATION

TWO COMPONENTS ADHESIVES HARDEN AT CONTACT. ONE TO FIVE MINUTES FIXING TIME. BETTER RESULT SEALING METALS, WOODS, CERAMICS, FERRITE AND SOME PLASTICS. HIGH IMPACT RESISTANT COUPLING.


GRADE
COLOUR
VISCOSITY
25°C mPa.s
POT-LIFE
Minutes
FUNCTIONAL STRENGTH
Minutes
SHEAR STRENGTH
DIN 53283 N/mm²
PEELING STRENGTH
N/mm
COUPLING TICKNESS
mm
33 - 00 
+ ACT.20
AMBER
20000 - 40000
1 - 4
30 - 60
18 - 30
2 - 3
0,05 - 1
30-55 
+ ACT 20
AMBER
75000 - 130000
1 - 3
10 - 20
12 - 25
3,5 - 5
0,05 - 0,50
33 - 47 
A + B
AMBER
5000 - 15000
1 - 3
30 - 60
15 - 25
3 - 5
0,05 - 1
33 - 47M 
+ ACT. 17
AMBER
8000 - 20000
1 - 3
30 - 60
15 - 25
3 - 5
0,05 - 1

*30-55 + ACT. 20 TEMPERATURE RANGE OF -40 °C + 150°C

PHYSICAL PROPERTIES

 

COMPOSITION ACRYLIC RESINS
TEMPERATURE RANGE -50 °C +120 °C
THERMAL CONDUCTIVITY ( W/mK ) 0,1
COEFFICIENT OF THERMAL EXPANSION ( 1/K ) 80 - 120 x 10 E-6
DIELECTRIC CONSTANT DIN 53483 ( Mhz ) 4,6

 